Ruthenium-iridium Oxide Coated Titanium Anode Rods for Water Heater

 A sacrificial rod (generally magnesium, aluminum, or zinc rod) is usually used in water heaters to increase its operating life and protect the lining of the water heater. However this sacrificial rod has to replace after 2 or 3 years. While MMO coated titanium rod can be used over 10 years. 



UTron had provided ruthenium-iridium oxide coated titanium anode rods for water heater to their Austria clients. Below is some parameter for reference. 


Rod Diameter:2 mm;

Rod length: 800 mm;

Coating: Ruthenium-iridium Oxide;

Coating Area:300 mm;

Operating life: 10 years;

Application: Water heater corrosion prevention; 

Exported Country: Austria.  


UTron had offered ruthenium-iridium oxide coated titanium anode rod to many Europe countries. The titanium rod and length can customized to meet your specific water tank. Samples are also available, feel free to contact us. 

标签：

评论

发表评论

此博客中的热门博文

MMO Linear Anode for Storage Tank Cathodic Protection Projects

 MMO linear anode distributes current uniformly over total area of the structure,it is independent of variations in soil resistivity and prevents accelerated coating disbondment. MMO linear anode mainly adopts in buried storage tank cathodic protection field. UTron had offered MMO linear anode forstorage tank cathodic protection projects to their customer from The United Arab Emirates. Below is some parameter for reference: Wire Diameter: 1.5mm; Anode Lengths:500 meter per roll; Cable: HMWPE; Current output:52mA/m; Operate Life: 40 years; Application: storage tank cathodic protection; Export Country: The United Arab Emirates.   UTron is an ISO9001 certified company with over 14 years production experience manufacturer, their products have exported to 62 countries in the whole world. With expert engineers and well after sale service, they have been enjoyed good reputation among their clients. 
发表评论
阅读全文

MMO Coated Titanium Rod for Hot Water Boilers Corrosion Prevention

  S acrificial anode   rod in a water heater have to replace about every three years. While MMO coated titanium anode can reach over ten years life span and it can eliminate lingering "rotten egg" odor   permanently. UTron had offered MMO coated titanium rods for hot water boilers corrosion prevention to their Poland clients. Below is some parameter for reference.   Rod Diameter: 3 mm; Rod length: 420mm ; Coating: Mixed Metal Oxide; MMO coated area: 42 0mm mm; Operating life: 10 years; Application: Water h eater cathodic protection; Exported Country: Poland.   UTron have manufactured MMO coated titanium anode for decades.With experienced engineers with over 30 years technical background, UTron can customize the coating, operating life, dimension operating life to meet your specific need. Any queries, please feel free to contact us.  
发表评论
阅读全文

Mixed Metal Oxide Ribbon Anode Width 6.35 mm, Thickness 0.635 mm

  Mixed Metal Oxide ribbon anode is generally fabricated with titanium substrate meets ASTM B265 in Grade1 or Grade2 and coated with IrO2/Ta2O5 mixed metal oxide. It is widely used in cathodic protection field for the low consumption rate and long design life.   UTron had provided mixed metal oxide ribbon anode width 6.35 mm , thickness 0.635 mm to their clients who are from The United Arab Emirates. Below is some parameter for reference. Width :   6.35 mm ; Thickness: 0.635 mm; Length:152m; Current O utput : 17 (mA/m) ; Operating Life:50 Year; Application: above ground storage tank cathodic protection; Exported Country: The United Arab Emirates.   UTron is a professional mixed metal oxide ribbon anode manufacturer with over 14 years production experience. Their products have been exported to over 62 countries in the world and enjoyed good reputation among their clients. Welcome to contact us for details. 
发表评论
阅读全文